410 Stainless Steel
410 stainless steel is a basic martensitic grade offering both exceptional wear and corrosion resistance. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it's hardened and tempered. 410 stainless steel is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more.
Standards
UNS S41000
ASTM A182
ASTM A276
ASTM A479
Composition(%)
Carbon 0.080-0.150
Chromium 11.50-13.50
Manganese 1.0 Max
Phosphorus 1.0 Max
Silicon 1.00 Max
Sulfur 0.030 Max
Round bar steel: 1mm to 1500mm diamter
Plate steel:0.1mm to 40mm
Width: 10mm to 2500mm
Length: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubes: OD: 3-1200mm, with wall thickness ranging from 0.5-55 mm.
|
410 Stainless Steel (annealed condition) |
|
Minimum Properties |
Ultimate Tensile Strength, psi |
65,000 |
|
Yield Strength, psi |
30,000 |
|
Elongation |
20 - 34% |
|
Rockwell Hardness |
B82 |
|
Chemistry |
Iron (Fe) |
86% |
|
Carbon (C) |
0.15% max |
|
Chrome (Cr) |
12.5% |
|
Manganese (Mn) |
1% max |
|
Phosphorus (P) |
0.04% max |
|
Sulphur (S) |
0.03%
|
Type 410 is used for springs, scrapers, fasteners, hardware brackets, furnace parts and burners. It is magnetic in all conditions. Tensile strength (as annealed) min. 65,000 PSI, yield strength minimum 30,000 PSI, and elongation in 2 inches at 20%. For solution annealing, slow controlled cooling from 1500/1600 F. For hardening, heat to 1700/1850 F. Quench in air or oil.