Hastelloy C-4

Hastelloy C-4

 

Hastelloy C-4 Chemical compostion:

Alloy

%

Ni

Cr

Mo

Fe

C

Mn

Si

Co

S

P

Ti

C-4

Min.

65

14

14

 

 

 

Max.

 

18

17

3.0

0.01

1.0

0.08

2.0

0.010

0.025

0.70


 

Hastelloy C-4 Physical properties:

Density

8.64 g/cm3

Melting point

1350-1400 centigrade degree


 

Hastelloy C-4 Alloy minimum mechanical properties in the room temperature:

Alloy
Tensile strength
Rm N/mm2
Yield strength
RP0.2N/mm2
Elongation
A5 %
C-4
783
365
55

 

Product forms of Hastelloy C4:
Sheet
Plate
Bar
Pipe & Tube (welded & seamless)
Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
Wire

 

HASTELLOY C-4 alloy is a nickel-chromium-molybdenum alloy with outstanding
high-temperature stability as evidenced by high ductility and corrosion resistance even
after aging in the 1200 to 1900Fahrenheit degree
 (649 to 1038 centigrade) range. This alloy resists the formation
of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable
for most chemical process applications in the as-welded condition. C-4 alloy also
has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to 1900Fahrenheit degree(1038 centigrade).

 

HASTELLOY C-4 alloy has exceptional resistance to wide variety of chemical process
environments. These include hot contaminated mineral acids, solvents, chlorine
and chlorine contaminated media (organic and inorganic), dry chlorine, formic and
acetic acids, acetic anhydride, and seawater and brine solutions.

 


HASTELLOY C-4 alloy can be forged, hot-upset, and impact extruded. Although the
alloy tends to work-harden, it can be successfully deep-drawn, spun, press formed or
punched. All of the common methods of welding can be used to weld HASTELLOY C-4
alloy, although the oxy-acetylene and submerged arc processes are not recommended
when the fabricated item is intended for use in corrosion service. Special precautions
should be taken to avoid excessive heat input.

 

 

 
Date:2011-3-20
Last:Hastelloy C(GB:NS333)
Next:Hastelloy C-2000

 

 

© 2003-2012 Shanghai Yikai Metal Products Co.,Ltd All rights reserved.   
Home | About us | Products | Case resources | Service | News center | Contact us
上海镒凯 2019-4-30 10:21:25
< a href="http://www.365webcall.com/">Online customer service
< a href="http://www.365webcall.com/">Online customer service system